Structural and magnetic properties of Co-doped ZnO thin films grown by ultrasonic spray pyrolysis method

Cobalt-doped ZnO thin films with several different percentage of Co from 0 up to 15 at% were synthesized via a cheap, simple and versatile method i.e. ultrasonic spray pyrolysis at atmospheric pressure and a substrate temperature of 350 °C. The structure of the as-prepared samples was characterized by X-ray diffraction (XRD), Raman spectroscopy and FTIR. The Co-doping effect is revealed by the presence of three additional peaks around 235, 470 and 538 cm−1 respect to the Raman spectra of the unsubstituted film. Fourier transform infrared spectroscopy (FTIR) put in evidence the decrease of the bond force constant f with increasing Co-doping. By ultra-violet visible near infrared (UV–Vis–NIR) spectroscopy on Co-doped samples it was possible to show the presence of additional absorption bands at approximately 570, 620 and 660 nm suggesting that Co2+ ions do not change their oxidation when substituted to zinc and the ZnO lattice does not change its wurtzite structure as well. Finally, all our samples exhibit a paramagnetic behavior without any trace of intrinsic room temperature ferromagnetism.