Skip to content
Home
About Us
Resources
Profiles Metrics
Authors Directory
Institutions Directory
Top Authors
Top Institutions
Top Sponsors
AI Digest
Contact Us
Menu
Home
About Us
Resources
Profiles Metrics
Authors Directory
Institutions Directory
Top Authors
Top Institutions
Top Sponsors
AI Digest
Contact Us
Home
About Us
Resources
Profiles Metrics
Authors Directory
Institutions Directory
Top Authors
Top Institutions
Top Sponsors
AI Digest
Contact Us
Menu
Home
About Us
Resources
Profiles Metrics
Authors Directory
Institutions Directory
Top Authors
Top Institutions
Top Sponsors
AI Digest
Contact Us
Publication Details
AFRICAN RESEARCH NEXUS
SHINING A SPOTLIGHT ON AFRICAN RESEARCH
Effect of temperature on the electrical properties of Zn
0.95
M
0.05
O (M = Zn, Fe, Ni)
Materials Science- Poland, Volume 32, No. 1, Year 2014
Notification
URL copied to clipboard!
Description
We report here the structural and electrical properties of Zn 0.95M0.05O ceramic varistors, M = Zn, Ni and Fe. The samples were tested for phase purity and structural morphology by using X-Ray diffraction XRD and scanning electron microscope SEM techniques. The current-voltage characteristics J-E were obtained by dc electrical measurements in the temperature range of 300 - 500 K. Addition of doping did not influence the hexagonal wurtzite structure of ZnO ceramics. Furthermore, the lattice parameters ratio c/a for hexagonal distortion and the length of the bond parallel to the c axis, u were nearly unaffected. The average grain size was decreased from 1.57 μm for ZnO to 1.19 μm for Ni sample and to 1.22 μm for Fe sample. The breakdown field EB was decreased as the temperature increased, in the following order: Fe > Zn > Ni. The nonlinear region was clearly observed for all samples as the temperature increased up to 400 K and completely disappeared with further increase of temperature up to 500 K. The values of nonlinear coefficient, a were between 1.16 and 42 for all samples, in the following order: Fe > Zn > Ni. Moreover, the electrical conductivity s was gradually increased as the temperature increased up to 500 K, in the following order: Ni > Zn > Fe. On the other hand, the activation energies were 0.194 eV, 0.136 and 0.223 eV for all samples, in the following order: Fe, Zn and Ni. These results have been discussed in terms of valence states, magnetic moment and thermo-ionic emission, which were produced by the doping, and controlling the potential barrier of ZnO. © Wroclaw University of Technology.
Authors & Co-Authors
Sedky, Ahmed
Egypt, Asyut
Faculty of Science
Saudi Arabia, Al-ahsa
King Faisal University
Mohamed, S. B.
Egypt, Asyut
Faculty of Science
Statistics
Citations: 13
Authors: 2
Affiliations: 2
Identifiers
Doi:
10.2478/s13536-013-0150-4
ISSN:
01371339
Research Areas
Environmental