PLZT phases near lead zirconate: 1. Determination by X-ray diffraction
Journal of the American Ceramic Society, Volume 88, No. 2, Year 2005
Notification
URL copied to clipboard!
The room temperature phase diagram of PLZT, (Pb,La)(Zr, Ti)O 3, or L\Z\T for L < 12 and T < 10 was constructed using X-ray diffraction patterns of sintered and crushed PLZT material. The orthorhombic antiferroelectric phase, a tetragonal phase, the rhombohedral (hexagonal) ferroelectric phases, and the mixed La-rich zone were identified. Increasing substitution of La for Pb in the structure of orthorhombic PLZT leads to a change toward the cubic structure with less anisotropy in a direction corresponding to the cubic 200 direction. At La above ∼ 8 to 11 mol%, La 2Zr 2O 7 appears in the mixed zone. With increasing substitution of Ti for Zr, there is no change toward a cubic structure as the anisotropy is nearly unchanged. However, at a Ti substitution above ∼ 6 mol%, a rhombohedral and a tetragonal structure appear.