Robust superhydrophobic TiO2@fabrics for UV shielding, self-cleaning and oil-water separation
Journal of Materials Chemistry A, Volume 3, No. 6, Year 2015
Notification
URL copied to clipboard!
Inspired by the surface geometry and composition of the lotus leaf with its self-cleaning behavior, in this work, a TiO2@fabric composite was prepared via a facile strategy for preparing marigold flower-like hierarchical TiO2 particles through a one-pot hydrothermal reaction on a cotton fabric surface. In addition, a robust superhydrophobic TiO2@fabric was further constructed by fluoroalkylsilane modification as a versatile platform for UV shielding, self-cleaning and oil-water separation. The results showed TiO2 particles were uniformly distributed on the fibre surface with a high coating density. In comparison with hydrophobic cotton fabric, the TiO2@fabric exhibited a high superhydrophobic activity with a contact angle of ∼160° and a sliding angle lower than 10°. The robust superhydrophobic fabric had high stability against repeated abrasion without an apparent reduction in contact angle. The as-prepared composite TiO2@fabric demonstrated good anti-UV ability. Moreover, the composite fabric demonstrated highly efficient oil-water separation due to its extreme wettability contrast (superhydrophobicity/superoleophilicity). We expect that this facile process can be readily and widely adopted for the design of multifunctional fabrics for excellent anti-UV, effective self-cleaning, efficient oil-water separation, and microfluidic management applications.