Untreated and alkali treated fibers from Alfa stem: effect of alkali treatment on structural, morphological and thermal features

Alfa stems are rich in cellulose and they are an inexpensive, easily renewable source of natural fibers with the potential for polymer reinforcement. However, large amounts of non-cellulosic materials, surface impurities and low degradation temperature make natural fibers less attractive for reinforcement of polymeric materials, unless they can be modified in a proper way. In this paper, Alfa stems were treated with NaOH solution with two different concentrations (1 and 5 wt%). Raw and treated stems were crushed to obtain fibers. Stems and fibers were characterized by scanning electron microscopy (SEM) and optical microscopy, respectively. Their crystallinity index was determined by X-ray diffraction, thermal stability by thermogravimetry and structural change by FT-IR and 13C NMR spectroscopy. Comparison and analysis of results confirmed some thermal, structural and morphological changes of the fibers after treatment due to removal of some non-crystalline constituents from the plant. SEM showed rougher surfaces after alkalization. FT-IR and 13C NMR showed a gradual improvement in cellulose level by alkali treatment with increasing NaOH concentration. The crystallinity index and thermal stability of treated Alfa fibers were also found to be improved.